Four novel unsymmetrical heteroacenes containing five-membered heterocycles (OPyN, TPyN, TPyC, TPyO) have been synthesized and characterized. The formed molecules exhibited twisted structures, determined by crystal analysis and showed blue/green fluorescence in dichloromethane and in thin film. Compounds OPyN and TPyN were selectively used as active ingredients, and the fabricated devices displayed promising electroluminescent performance.Keywords: electroluminescence; optical property; polycyclic aromatic hydrocarbons; single crystal; twistacene;

The fabrication of printed high-performance and environmentally stable n-type single-walled carbon nanotube (SWCNT) transistors and their integration into complementary (i.e., complementary metal–oxide–semiconductor, CMOS) circuits are widely recognized as key to achieving the full potential of carbon nanotube electronics. Here, we report a simple, efficient, and robust method to convert the polarity of SWCNT thin-film transistors (TFTs) using cheap and readily available ethanolamine as an electron doping agent. Printed p-type bottom-gate SWCNT TFTs can be selectively converted into n-type by deposition of ethanolamine inks on the transistor active region via aerosol jet printing. Resulted n-type TFTs show excellent electrical properties with an on/off ratio of 106, effective mobility up to 30 cm2 V–1 s–1, small hysteresis, and small subthreshold swing (90–140 mV dec–1), which are superior compared to the original p-type SWCNT devices. The n-type SWCNT TFTs also show good stability in air, and any deterioration of performance due to shelf storage can be fully recovered by a short low-temperature annealing. The easy polarity conversion process allows construction of CMOS circuitry. As an example, CMOS inverters were fabricated using printed p-type and n-type TFTs and exhibited a large noise margin (50 and 103% of 1/2 Vdd = 1 V) and a voltage gain as high as 30 (at Vdd = 1 V). Additionally, the CMOS inverters show full rail-to-rail output voltage swing and low power dissipation (0.1 μW at Vdd = 1 V). The new method paves the way to construct fully functional complex CMOS circuitry by printed TFTs.Keywords: ethanolamine; n-type and p-type; printed CMOS inverters; printed thin film transistors; selective polarity conversion; sorted semiconducting carbon nanotube;

Two innovative research studies are reported in this paper. One is the sorting of semiconducting carbon nanotubes and ink formulation by a novel semiconductor copolymer and second is the development of CMOS inverters using not the p-type and n-type transistors but a printed p-type transistor and a printed ambipolar transistor. A new semiconducting copolymer (named P-DPPb5T) was designed and synthesized with a special nonlinear structure and more condensed conjugation surfaces, which can separate large diameter semiconducting single-walled carbon nanotubes (sc-SWCNTs) from arc discharge SWCNTs according to their chiralities with high selectivity. With the sorted sc-SWCNTs ink, thin film transistors (TFTs) have been fabricated by aerosol jet printing. The TFTs displayed good uniformity, low operating voltage (±2 V) and subthreshold swing (SS) (122–161 mV dec−1), high effective mobility (up to 17.6–37.7 cm2 V−1 s−1) and high on/off ratio (104–107). With the printed TFTs, a CMOS inverter was constructed, which is based on the p-type TFT and ambipolar TFT instead of the conventional p-type and n-type TFTs. Compared with other recently reported inverters fabricated by printing, the printed CMOS inverters demonstrated a better noise margin (74% 1/2 Vdd) and was hysteresis free. The inverter has a voltage gain of up to 16 at an applied voltage of only 1 V and low static power consumption.

In this work, a new poly(9,9-dioctylfluorene) (PFO) derivative (named PFIID) with the large conjugated planar surfaces was designed and synthesized, and the ability to sort sc-SWCNTs was investigated in detailed. The absorption spectra of sorted SWCNT solutions demonstrated that PFIID exhibited the ability to selectively and efficiently sort sc-SWCNTs from commercial arc discharge carbon nanotubes. The underlying separation mechanism was studied with the aid of photoluminescence excitation (PLE) spectra and the molecular dynamic simulation. It was found that the simulation results agreed well with the experimental data. PFIID-sorted sc-SWCNTs were acted as the channel materials to construct printed thin-film transistors (TFTs) and nitrogen dioxide gas sensors. Printed SWCNT TFTs exhibited superior performance with good uniformity, high on/off ratios (∼106), high effective hole mobility (∼29.8 cm2 V−1 s−1) and small subthreshold swing (SS) (142–163 mV/dec) at low operating voltage (±2 V). NO2 gas sensors also showed good performance with high sensitivity (ΔR/Ro∼96%), fast response (30 s), good stability and the recovery time of 30 s when exposed to 60 ppm NO2 at room temperature. Both of the sensitivity and recovery time are one of the best performances reported for NO2 gas sensors at room temperature.

•A series of dibenzotetracene derivatives were synthesized.•Single crystal analysis shows these compounds have twisted structures.•Electroluminescent devices were fabricated to assess the performance of the new dibenzotetracene.A series of dibenzotetracene derivatives containing different substituents at the 11-,12-positions have been successfully synthesized and characterized. Single crystal X-ray analysis indicates that the new molecules have a twisted structure, which can effectively decrease the intermolecular aggregation in the solid-state. The effect of both substituent and packing on the corresponding physical properties was also investigated. In addition, organic light-emitting diodes doped with 11,12-difluoro-9,14-diphenyl-dibenzo[de,qr]tetracene into the emitter 9,9′-(1,3-phenylene)bis-9H-carbazole were fabricated and exhibit good performance.

In this report printed thin film transistors and logic circuits on flexible substrates are reported. The top-gate thin film transistors were made of the sorted semiconducting single-walled carbon nanotubes (sc-SWCNTs) ink as channel material and printed silver lines as top electrodes and interconnect. 5 nm HfOx thin films pre-deposited on PET substrates by atomic layer deposition (ALD) act as the adhesion layers to significantly improve the immobilization efficiency of sc-SWCNTs and environmental stability. The immobilization mechanism was investigated in detail. The flexible partially-printed top-gate SWCNT TFTs display ambipolar characteristics with slightly strong p-type when using 50 nm HfOx thin films as dielectric layer, as well as the encapsulation layer by atomic layer deposition (ALD) at 120 °C. The hole mobility, on/off ratio and subthreshold swing (SS) are ∼46.2 cm2 V−1 s−1, 105 and 109 mV per decade, respectively. Furthermore, partially-printed TFTs show small hysteresis, low operating voltage (2 V) and high stability in air. Flexible partially-printed inverters show good performance with voltage gain up to 33 with 1.25 V supply voltage, and can work at 10 kHz. The frequency of flexible partially-printed five-stage ring oscillators can reach 1.7 kHz at supply voltages of 2 V with per stage delay times of 58.8 μs. This work paves a way to achieve printed SWCNT advanced logic circuits and systems on flexible substrates.

The precise placement and efficient deposition of semiconducting single-walled carbon nanotubes (sc-SWCNTs) on substrates are challenges for achieving printed high-performance SWCNT thin-film transistors (TFTs) with independent gates. It was found that the wettability of the substrate played a key role in the electrical properties of TFTs for sc-SWCNTs sorted by poly[(9,9-dioctylfluorene-2,7-diyl)-co-(1,4-benzo-2,1,3-thiadiazole)] (PFO-BT). In the present work we report a simple and scalable method which can rapidly and selectively deposit a high concentration of sc-SWCNTs in TFT channels by aerosol-jet-printing. The method is based on oxygen plasma treatment of substrates, which tunes the surface wettability. TFTs printed on the treated substrates demonstrated a low operation voltage, small hysteresis, high mobility up to 32.3 cm2 V–1 s–1, and high on/off ratio up to 106 after only two printings. Their mobilities were 10 and 30 times higher than those of TFTs fabricated on untreated and low-wettability substrates. The uniformity of printed TFTs was also greatly improved. Inverters were constructed by printed top-gate TFTs, and a maximum voltage gain of 17 at Vdd = 5 V was achieved. The mechanism of such improvements is that the PFO-BT-functionalized sc-SWCNTs are preferably immobilized on the oxygen plasma treated substrates due to the strong hydrogen bonds between sc-SWCNTs and hydroxyl groups on the substrates.Keywords: electrical properties; printed thin-film transistors; single-walled carbon nanotube; sorted; uniformity; wettability

A simple and scalable method has been developed to preferentially eliminate metallic species in several commercial single-walled carbon nanotubes (SWCNTs), such as CoMoCAT 65, CoMoCAT 76, CG 200, HiPco, and arc discharge (P2) SWCNTs, using 4-nitrobenzenediazonium salts by tuning the types and concentrations of surfactants in aqueous solutions. The selectivity in commonly used surfactant solutions was confirmed by ultra violet-visible-near infrared spectra, Raman spectra and electrical characterization. Good-performance printed thin-film transistors (TFTs) were obtained by inkjet printing. The printed TFTs exhibited excellent electrical properties with effective mobility and on/off ratio upto 3.54 cm2 V−1 s−1 and 3 × 105, respectively. This method does not require complicated reaction conditions and tedious purification procedure, therefore, promises low-cost production of high-performance printed TFT devices for electronic applications.

In this work, a simple and rapid method to selectively sort semiconducting-SWCNTs (sc-SWCNTs) with large diameters using regioregular poly(3-dodecylthiophene) (rr-P3DDT) is presented. The absorption spectra and Raman spectra demonstrated that metallic species of arc discharge SWCNTs were effectively removed after interaction with rr-P3DDT in toluene with the aid of sonication and centrifugation. The sorted sc-SWCNT inks have been directly used to fabricate thin film transistors (TFTs) by dip-coating, drop-casting and inkjet printing. TFTs with an effective mobility of ∼34 cm2 V−1 s−1 and on–off ratios of ∼107 have been achieved by dip coating and drop casting the ink on SiO2/Si substrates with pre-patterned interdigitated gold electrode arrays. The printed devices also showed excellent electrical properties with a mobility of up to 6.6 cm2 V−1 s−1 and on–off ratios of up to 105. Printed inverters based on the TFTs have been constructed on glass substrates, showing a maximum voltage gain of 112 at a Vdd of −5 V. This work paves the way for making printable logic circuits for real applications.

In this work, a simple and effective method has been developed to selectively separate large-diameter semiconducting-SWCNTs (sc-SWCNTs) from commercial arc discharge SWCNTs using (9,9-dioctylfluorene-co-bithiophene) (F8T2). The role of solvents in the separation and dispersion processes was studied. It has been proved that sc-SWCNTs mixed in arc discharge SWCNTs can be selectively sorted by F8T2 in toluene, xylene, or m-xylene with the aid of sonication and centrifugation, and the molecular dynamic simulation also agrees with the experiment results. The resulted sc-SWCNTs dispersion solution was used as a printable ink to print thin-film transistors (TFTs) via an aerosol jet printer. The printed TFTs showed good uniformity and electrical properties with on current up to 10–3 A, effective mobility up to 42.1 cm2 V–1 s–1 (±1.2 cm2 V–1 s–1), and on/off ratio of ∼107 after only four cycles of repeated printing. In addition, all of the printed devices exhibited rapid photocurrent response to light irradiation.

In this manuscript, we developed a high-performance, printable and water-based semiconducting SCNT ink, and fabricated all-printed chemically functionalized CoMoCat 76 SCNT thin film transistors (TFTs) on flexible substrates via a suite of printing technologies. The metallic species in the pristine CoMoCat 76 SCNTs were effectively eliminated by organic radicals, and the functionalized SCNTs were characterized by UV-Vis-NIR spectroscopy and Raman spectra. The high quality, printable and water-based functionalized SCNT inks were obtained by tuning the ink ingredients, such as the concentrations of surfactants and additives. The printing methods we investigated include inkjet printing, aerosol jet printing and a hybrid with nanoimprinting. Large area source and drain electrode patterns were first fabricated on flexible substrates by a hybrid printing method, and then the optimal SCNT ink was printed on the channel of the TFT devices by ink-jet printing. Subsequently, the silver side-gate electrode and ion gel dielectric layer were deposited by aerosol jet printing. The all-printed flexible TFTs exhibited an effective mobility up to 1.5 cm2 V−1 s−1 and an on/off ratio up to 4 × 103. This work opens up a way to fabricate scalable and all-printed flexible electronics, and it is of benefit to generalize the practical applications of flexible electronics in the future.

A simple and scalable method to print high performance thin-film transistors (TFTs) with high yield by an aerosol jet printer has been developed, using water-based and chemically functionalized single-walled carbon nanotube (SCNT) inks as the semiconducting layer. The absorption spectra, Raman spectra and photoluminescence excitation (PLE) spectra of the SCNT ink indicated that metallic species and small diameter semiconducting species in CoMoCat 76 were effectively eliminated after reaction with 2,2-azobisisobutyronitrile (AIBN) in dimethyformamide (DMF). The functionalized SCNTs were dispersed in 1% SDS aqueous solution, and the as-prepared SCNTs inks were directly used to print TFTs using an aerosol jet printing system without any additional purification. Printed TFTs with high yield were obtained by tuning the concentrations of SCNTs and surfactants in the inks. The printed side-gate and bottom-gate TFTs exhibited the effective mobility of ∼1 cm2 V−1 s−1 and an on/off ratio over 103. In addition, these printed TFTs were hysteresis-free and able to operate at low-voltage when using printable high-capacitance ion gel as the dielectric layer. The new method has opened the route to fabricate all-printed SCNT TFTs on flexible substrate with high performance.

In this manuscript, we developed a high-performance, printable and water-based semiconducting SCNT ink, and fabricated all-printed chemically functionalized CoMoCat 76 SCNT thin film transistors (TFTs) on flexible substrates via a suite of printing technologies. The metallic species in the pristine CoMoCat 76 SCNTs were effectively eliminated by organic radicals, and the functionalized SCNTs were characterized by UV-Vis-NIR spectroscopy and Raman spectra. The high quality, printable and water-based functionalized SCNT inks were obtained by tuning the ink ingredients, such as the concentrations of surfactants and additives. The printing methods we investigated include inkjet printing, aerosol jet printing and a hybrid with nanoimprinting. Large area source and drain electrode patterns were first fabricated on flexible substrates by a hybrid printing method, and then the optimal SCNT ink was printed on the channel of the TFT devices by ink-jet printing. Subsequently, the silver side-gate electrode and ion gel dielectric layer were deposited by aerosol jet printing. The all-printed flexible TFTs exhibited an effective mobility up to 1.5 cm2 V−1 s−1 and an on/off ratio up to 4 × 103. This work opens up a way to fabricate scalable and all-printed flexible electronics, and it is of benefit to generalize the practical applications of flexible electronics in the future.

A simple and scalable method to print high performance thin-film transistors (TFTs) with high yield by an aerosol jet printer has been developed, using water-based and chemically functionalized single-walled carbon nanotube (SCNT) inks as the semiconducting layer. The absorption spectra, Raman spectra and photoluminescence excitation (PLE) spectra of the SCNT ink indicated that metallic species and small diameter semiconducting species in CoMoCat 76 were effectively eliminated after reaction with 2,2-azobisisobutyronitrile (AIBN) in dimethyformamide (DMF). The functionalized SCNTs were dispersed in 1% SDS aqueous solution, and the as-prepared SCNTs inks were directly used to print TFTs using an aerosol jet printing system without any additional purification. Printed TFTs with high yield were obtained by tuning the concentrations of SCNTs and surfactants in the inks. The printed side-gate and bottom-gate TFTs exhibited the effective mobility of ∼1 cm2 V−1 s−1 and an on/off ratio over 103. In addition, these printed TFTs were hysteresis-free and able to operate at low-voltage when using printable high-capacitance ion gel as the dielectric layer. The new method has opened the route to fabricate all-printed SCNT TFTs on flexible substrate with high performance.