Co-reporter:Maoqiu Wang, Eiji Akiyama, Kaneaki Tsuzaki
Scripta Materialia 2005 Volume 52(Issue 5) pp:403-408
Publication Date(Web):March 2005
DOI:10.1016/j.scriptamat.2004.10.023
The maximum tensile stress of hydrogen pre-charged specimens during slow strain rate test decreased in a power law manner with increasing diffusible hydrogen content in the presence of intergranular fracture. The lower hydrogen degradation susceptibility at a lower strength level is due to delayed onset of intergranular fracture.